          金融业型聚氯乙烯/人口腈复合物弹性体绝缘料 W-7082 W-9082 W-0582
          Lead-free Elastomeric PVC / NBR Insulation Compound...
          生肖印:0

          菜价:¥

          表明:如您对该产品感兴趣,请在此投入您的无绳电话机号将资产产品的地点 发送至您手机上。
          Product D escription 产品描述
          Lead-free elastomeric PVC/NBR insulation compounds are granule compounds which are manufactured with mixing, plasticizing and pelletizing processes. They regard advanced PVC resin and nitrile-butadiene rubberas the basic raw material, and add special plasticizer, stabilizer, flame retardant and other accessory ingredients.
          金融业型聚氯乙烯/人口腈复合物弹性体绝缘料是以优质聚氯乙烯树脂和丁腈橡胶为基料,进入特种增塑剂、稳定剂、阻燃剂等助剂,经混合、塑化、造粒而成的粒状电缆料。
           
          Characteristics and Application 特色及用途
          These products have good oil-resistant property, soft and flexible, and good processability. They can meet RoHS Standard. They are mainly used for the insulation of oil-resistant cables, elevator cables, oil-resistant soft wires of dust cleaner, heavy soft cables and crane cables.
          产品具有优秀的耐油性、服务性和柔软性,加工性能优异,符合RoHS金融业标准。根本用于有耐油要求的电线电缆、电梯电缆、耐油吸尘器软线、大型软线、起重机电缆等绝缘材料。
           
          Processing Indicator 加工工艺
          Recommend to use of single-screw extruders with L/D= 20-25.
          提议使用普通长径比为20-25的单螺杆挤出机进行生产。
          Model
          牌号
          Machine Barrel Temperature
          飞机筒温度
          Molding Temperature
          机头温度
          W-7082 / W-9082 / W-0582
          145-170℃
          165-175℃
           

          Physical and Electrical Properties
          机械物理性能及电性能指标

          热电竞-热电竞入口-热电竞竞猜-外围-热电竞 懂你的竞猜网站

          考试项目

          Unit
          单位
          Technical Requirements
          艺术要求
          W-7082
          W-9082
          W-0582
          Density
          比重
          \
          ≤1.40
          ≤1.40
          ≤1.40
          Tensile Strength
          拉伸强度
          MPa
          ≥12.5
          ≥12.5
          ≥12.5
          Elongation at Break
          断裂伸长率
          %
          ≥180
          ≥180
          ≥180
          Thermal Aging
          热老化试验
          \
          80℃×168h
          100℃×240h
          135℃×168h
          Tensile Strength Variation
          拉伸强度变化率
          %
          ±40
          ±40
          ±40
          Elongation Variation
          断裂伸长率变化率
          %
          ±40
          ±40
          ±40
          Dielectric Strength
          介电强度
          MV/m
          ≥20
          ≥20
          ≥20
          200℃Thermal Stability
          200℃时热平静时间
          min
          ≥80
          ≥120
          ≥120
          20℃Volume Resistivity
          20℃时体积电阻率
          Ω.m
          ≥1×10 11
          ≥1×10 11
          ≥1×10 11
          Brittle Temperature with Impact
          碰上脆化温度
          -30
          -30
          -30
          Oil Resistance
          耐油性能(ASTM 902)
          Temperature of Test考试温度
          70
          100
          100
          Time of Test
          考试时间
          h
          24
          24
          24
          Tensile Strength Variation
          拉伸强度变化率
          %
          ±40
          ±40
          ±40
          Elongation Variation
          断裂伸长率变化率
          %
          ±40
          ±40
          ±40
          Hardness
          强度
          Shore A
          ≤75
          ≤75
          ≤75